Rheological Properties and Microscopic Mechanisms of Composite-Modified Asphalt with Direct Coal Liquefaction Residue

To enhance the overall performance of direct coal liquefaction residue (DCLR)-modified asphalt, particularly its low-temperature cracking resistance, SBS and aromatic oil were employed for composite modification. Nine composite-modified asphalt formulations were prepared based on an orthogonal experimental design. High-and low-temperature rheological properties and microstructure of all modified asphalts were systematically evaluated using a dynamic shear rheometer (DSR), a bending beam rheometer (BBR), Fourier-transform infrared spectroscopy (FTIR), and scanning electron microscopy (SEM). The results indicate that composite modification significantly enhanced the high-temperature performance of the asphalt. Modified asphalt labeled as Sample No. 9 (9% DCLR, 4% SBS, and 6% aromatic oil) demonstrated the minimal non-recoverable creep compliance (Jnr) value of 0.58 kPa−1 at 64 °C, indicating a 78.6% decrease relative to the matrix asphalt. In terms of low-temperature performance, Sample No. 3 satisfied the Superpave cracking resistance criterion, exhibiting a creep rate (m-value) of 0.312 at −12 °C. It was revealed by FTIR analysis that the interaction between the composite modifier and the base asphalt was mainly physical blending, and no new functional groups were generated either before or after aging. The improvement in performance was attributed to the physical compatibility and structural reorganization among the components. Microstructural analysis revealed that the uniform dispersion of modifiers in matrix asphalt and the subsequent formation of a dense micelle structure after aging contributed to the enhanced macroscopic performance. This study provides theoretical and technical support for the high-value application of DCLR in asphalt pavements.