The electrocatalytic activity of electrodeposited Pt100–xNix thin films toward the oxygen reduction reaction (ORR) in perchloric acid was studied for x ranging between 2 and 95. The alloy composition was controlled by the potential applied during deposition. XRD and EDS were used to examine the structure and composition of the films before and after ORR measurements. Significant dealloying was evident for films with x > 45, and substantial shrinkage of the film thickness accompanied dealloying for films with x > 55. The onset of significant shrinkage occurs near the parting limit reported for bulk dealloying of fcc solid solutions. A maximum ORR specific activity of 2.8 mA/cm2 at 0.900 V RHE was observed for alloys between Pt45Ni55 and Pt55Ni45. This represents an enhancement factor of 4.7 compared to electrodeposited Pt, thereby matching the best published results reported for Pt–Ni nanoparticles and thin films. A peak ORR mass activity of 0.78 A/mgPt at 0.900 V RHE was observed for alloy film compositions between Pt38Ni62 and Pt45Ni55. In comparison to electrodeposited Pt, these films exhibit a 10-fold improvement in mass activity.
No takes yet. Share an insight, caveat, or question.
Liu et al. (2012) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: