Bone tissue engineering requires biomimetic materials; however, pure polylactic acid (PLA) exhibits limited osteoinductivity and produces acidic byproducts upon degradation. To address these limitations, this study fabricated PLA scaffolds using fused-deposition modeling (FDM) with four distinct lattice structures (rectangular, triangular, gyroid, and 3D honeycomb) and incorporated hydroxyapatite (HA) at 0, 10, 20, and 30 wt% via injection molding. Mechanical properties were evaluated via compression, three-point bending, and tensile testing. The results revealed that increasing HA content significantly reduced structural strength and increased brittleness across all test modes. Specifically, specimens with 30 wt% HA exhibited a 70.8% reduction in bending strength relative to pure PLA (from 58.60 MPa to 17.07 MPa), while tensile strength decreased by 46.1% at just 10 wt% HA (from 37.54 MPa to 20.23 MPa). Although the triangular lattice achieved the highest absolute compressive load, the rectangular lattice provided a superior load-to-weight ratio and greater plastic deformation capacity before fracture. Consequently, these findings indicate that the rectangular pattern at 70% infill density combined with HA addition limited to ≤10 wt% represents the most mechanically balanced design for bone defect repair applications. Based on the mechanical characterization performed in this study, and drawing on published evidence regarding the biological properties of PLA/HA composites, these scaffolds represent a mechanically promising candidate for further evaluation in bone tissue regeneration. Biological validation through in vitro and in vivo studies is required before clinical relevance can be established.
Budi et al. (Fri,) studied this question.