Synthesis of Fully Dense Monoclinic Zirconia Ceramics via Ternary Sintering Aids

Fully dense monoclinic zirconia ceramics were successfully fabricated by pressureless sintering and/or HIP. Although monoclinic zirconia exhibits unique physicochemical properties, fabrication of fully dense polycrystalline bodies has remained challenging due to catastrophic volume expansion during the tetragonal-to-monoclinic transformation. By introducing a synergistic ternary (Ga2O3-ZnO-TiO2) sintering aid, a relative density exceeding 99.6% with an average grain size of 0.5–2 µm was achieved by sintering under an oxygen atmosphere at 1070 °C for 3–100 h, well below the phase-transition temperature. X-ray diffractometry confirmed a single-phase monoclinic structure. Subsequent hot isostatic pressing at 1080 °C and 180 MPa for 2 h eliminated residual porosity, yielding a 4-point bending strength of 328 MPa, a fracture toughness of 2.7 MPa·m0.5, and a Vickers hardness HV1 of 805. This monoclinic zirconia ceramic exhibited ~30% total transmittance, while in-line transmittance remained below 0.1% due to intrinsic birefringence of the monoclinic lattice. These results established a low-temperature route for densifying phase-sensitive ceramics while achieving long-term stability.