This study presents the development of biocompatible antistatic nanofibrous composite yarns via a scalable AC electrospinning method, incorporating ultrasonicated expanded graphite (uEG) and PEDOT:PSS into polyamide (PA), polyvinyl butyral (PVB), and polyvinyl alcohol (PVA) matrices. TGA confirmed high filler retention during electrospinning. Electrical measurements showed that the addition of uEG and micrographite reduced single-yarn resistance by up to two orders of magnitude compared with neat polymers, yielding normalised resistivities as low as ~105–106 Ω·m and conductivities in the 10−7–10−5 S/m range, suitable for antistatic and sensing applications. However, the large filler–fibre size mismatch and highly porous yarn architecture limited the formation of continuous conductive networks, and mechanical tests revealed strength reductions of up to 70–80% at the highest PVB filler loadings. XRD confirmed a reduction in crystallinity with filler addition, PEDOT:PSS enhanced polymer chain nucleation and thus mechanical properties. Cytotoxicity assays demonstrated that uEG, micrographite, and PEDOT:PSS significantly improved cell viability compared with non-crosslinked PVA, with several PVB-based and PVA/uEG composites showing viability statistically comparable to the DMEM control (>70%) while remaining significantly higher than the Triton positive control. Overall, this work establishes an AC-electrospun route to antistatic nanofibrous yarns that combine high filler retention with enhanced biocompatibility.
Coetzee et al. (Sun,) studied this question.