Development and Characterization of Metal-Insulator-Metal Capacitors with SiN x Thin Films by Plasma-Enhanced Chemical Vapor Deposition

We report the fabrication of high breakdown voltage metal-insulator-metal (MIM) capacitors with 200-nm silicon nitride deposited by plasma-enhanced chemical vapor deposition with 0.957 SiH4/NH3 gas mixing rate, 0.9 Torr working pressure, and 60 W rf power at 250° C chamber temperature. Some optimized mechanisms such as metal source wiping, pre-melting and evaporation rate adjustment are used for increasing the yield of the MIM capacitors. N2 annealing and O2/H2 plasma pre-deposition treatment is proposed to increase the reliability of the MIM capacitors in high-temperature, high-pressure, and high-humidity environments. A 97% yield and up to 148 V breakdown voltage of a 13.06 pF MIM capacitor with 0.04 mm2 die area can be fabricated.