The hydrogen oxidation reaction (HOR) in alkaline electrolyte was conducted on carbon-supported Ru nanoparticles (Ru/C) of which size was controlled in the range from approximately 2 to 7 nm. The HOR activity of Ru/C normalized by the metal surface area showed volcano shaped dependence on the particle size with a maximum activity at approximately 3 nm. The HOR activity of approximately 3 nm Ru/C was higher than commercially available Pt nanoparticles (ca. 2 nm) supported on carbon. The structural analysis of Ru/C using Cs-corrected scanning transmission electron microscopy with atomic resolution revealed the unique structural change of Ru/C different from Pt/C: Ru nanoparticle structure changed from amorphous-like structure below 3 nm to metal nanocrystallite with roughened surface at approximately 3 nm and then to that with well-defined facets above 3 nm, although Pt/C kept well-defined facets even at approximately 2 nm. It is proposed that the generation of unique structure observed on approximately 3 nm Ru nanoparticles, that is, long bridged coordinatively unsaturated Ru metal surface atoms on its nanocrystallite, is a key to achieve high HOR activity.
No takes yet. Share an insight, caveat, or question.
Ohyama et al. (2013) studied this question.
Synapse has enriched 10 related papers. Consider them for comparative context: