Development and Characterization of CoCrMo/xCu Composites Fabricated by Powder Metallurgy

This study aims to develop CoCrMo/xCu composites through liquid phase sintering. The primary focus is on investigating how the addition of copper influences sintering kinetics, microstructure, and mechanical properties. The copper volume fraction ranged from 10 to 25 wt.% relative to CoCrMo. Sintering was conducted at 1150 °C under an argon atmosphere. Characterization methods included scanning electron microscopy, computed microtomography, and X-ray diffraction analysis. It was observed that molten copper, which forms upon reaching its melting temperature, can fill the interparticle spaces left by CoCrMo particles in the green compacts. During sintering, densification is further enhanced by the dissolution of CoCrMo, resulting in the formation of intermetallic phases enriched in Cr and Mo, as well as a ternary Co-Cr-Cu compound. Both densification and intermetallic formation contribute to increased microhardness as Cu content rises. It is concluded that the CoCrMo/25Cu composite exhibits the best mechanical and corrosion properties because its densification was improved by the Cu liquid.