Effect of Microstructure Development on the Corrosion Behavior of EN AW-5083 in As-Cast and Homogenized Conditions

The corrosion behavior of the EN AW-5083 alloy was investigated due to its widespread use in marine and transportation applications. The study examined the influence of microstructure development on corrosion behavior in both as-cast and homogenized conditions. Thermodynamic calculations, differential scanning calorimetry, and metallographic characterization were used to analyze solidification and microstructure development, while electrochemical testing was applied to evaluate corrosion resistance in a solution simulating severe outdoor exposure conditions, primarily marine, industrial, and transportation environments. The results show that the as-cast microstructure contains a heterogeneous distribution of anodic and cathodic intermetallic phases, which promotes localized corrosion. Homogenization at 520 °C led to the dissolution of the Al8Mg5 (β) phase, resulting in reduced sensitization effects and slightly improved corrosion resistance. However, high corrosion rates were observed in both metallurgical conditions, indicating limited resistance under the applied testing conditions. The study confirms that microstructural modification through homogenization influences corrosion mechanisms in EN AW-5083.