Experimental and Theoretical Investigation of the κ-Phase (Ag2Mg5) in the Ag-Mg System

The present study extends the investigation of thermodynamic properties of phases in the silver–magnesium binary system, with particular emphasis on the κ-Ag2Mg5 phase, for which available literature data remain scarce. The work is divided into two parts. The experimental section comprises the synthesis of the κ phase from high-purity Ag and Mg, followed by its characterisation using scanning electron microscopy (SEM) and X-ray diffraction (XRD). The synthesised material was subsequently used for calorimetric determination of the standard enthalpy of formation employing the drop solution method. Measurements were carried out in two experimental series (A and B), using two different metallic solvents (Al and Sn), at temperatures of 1020 K and 689 K. The enthalpy of formation obtained in both series was −14.4 ± 0.32 and −14.5 ± 0.42 kJ/mol at., respectively. In addition, the limiting partial enthalpy of solution of liquid Ag in liquid Al was determined calorimetrically and its average value is equal 7.1 ± 0.7 kJ/mol. The theoretical part of the study involved ab initio calculations of defect formation energies. The obtained results show good agreement with available literature data and provide a consistent interpretation of the observed non-stoichiometry of the κ-phase.