Gold-free contacts on AlxGa1-xN/GaN high electron mobility transistor structure grown on a 200-mm diameter Si(111) substrate

The authors report on the fabrication and characterization of low-temperature processed gold-free Ohmic contacts for AlxGa1−xN/GaN high electron mobility transistors (HEMTs). The HEMT structure grown on a 200-mm diameter Si(111) substrate is used in this study. Using the Ti/Al/NiV metal stack scheme, the source/drain Ohmic contact optimization is accomplished through the variation of Ti/Al thickness ratio and thermal annealing conditions. For an optimized Ti/Al stack thickness (20/200 nm) annealed at 500 °C for 30 s with smooth contact surface morphology, a specific contact resistivity of ∼6.3 × 10−6 Ω cm2 is achieved. Furthermore, with gold-free Ni/Al gates, the fabricated HEMTs exhibit ION/IOFF ratio of ∼109 and a subthreshold swing of ∼71 mV/dec. The demonstrated gold-free contact schemes thus provide a solution toward the implementation of GaN-based HEMT process on a Si foundry platform.