Tool Reuse by Electrolytic Stripping and Re-Coating: Comparative Study of PVD Nitrides in Turning AISI 4340 Steel

The reuse of WC–Co cutting inserts is a relevant strategy to reduce tooling costs and the consumption of critical raw materials, such as W and Co. Still, the effect of stripping and re-coating cycles on tool performance remains largely unexplored. This work investigates the wear behavior of carbide inserts coated with four PVD nitride systems—CrN, TiAlN, TiAlCrN, and TiAlCrSiN—during CNC turning of AISI 4340 steel. A single cutting edge was subjected to two complete reuse cycles consisting of machining six workpieces, electrolytic stripping of the worn coating, and PVD re-deposition. Tool wear and surface integrity were evaluated by 3D optical profilometry, roughness measurements, and SEM/EDS analysis. CrN exhibited progressive crater and flank wear with large material-loss volumes and increasing roughness. TiAlN exhibited pronounced built-up edge/layer formation, resulting in mixed adhesion–spallation behavior and degradation of roughness in the second cycle. TiAlCrN developed stable adhesive layers with limited coating loss, and after re-coating, its roughness decreased from ~2.7 µm to ~1.0 µm. The most complex coating, TiAlCrSiN, provided the lowest roughness (~1.3–1.6 µm) and the smallest wear volumes in both cycles, associated with a fine Al–Si-induced nanostructure and improved oxidation resistance. The results demonstrate that multicomponent nanostructured coatings, particularly TiAlCrN and TiAlCrSiN, can withstand at least one stripping and re-coating cycle without performance loss, supporting the feasibility of controlled insert reuse in turning AISI 4340 steel.