Hydrothermal-Assisted Sulfuric Acid Activation of Date Seed-Derived Carbon for High-Performance Supercapacitor Electrodes and Hydrogel Electrolytes

This study aims to develop a sustainable, low-cost, and high-performance supercapacitor electrode by valorizing waste date seeds (Phoenix dactylifera) into activated carbon and integrating it with a polymer-based hydrogel electrolyte. Waste date seeds were successfully converted into high-performance activated carbon through hydrothermal carbonization followed by sulfuric acid (H2SO4) chemical activation. The obtained date seed activated carbon (DSAC) was applied as an electrode material and incorporated into a hydrogel electrolyte for supercapacitor applications. Structural, thermal, and morphological analyses using SEM, FTIR, XRD, and TGA confirmed the formation of a predominantly microporous carbon framework enriched with oxygen-containing functional groups, indicating effective carbonization and activation. The porous structure and surface chemistry contributed to enhanced electrochemical behavior. The electrochemical behavior of the prepared DSAC electrode was investigated through cyclic voltammetry (CV) and galvanostatic charge–discharge (GCD) analyses. The material exhibited a highest specific capacitance of 179 F g−1 at a scan rate of 5 mV s−1 and 159 F g−1 at a current density of 0.2 A g−1, demonstrating reliable and stable capacitive characteristics suitable for biomass-derived carbon-based supercapacitor applications. The device also exhibited excellent cycling stability over 5500 cycles, confirming long-term durability. The results demonstrate a promising and environmentally friendly strategy for advanced energy storage systems. Furthermore, the sustainability and cost-effectiveness of the proposed approach are attributed to the utilization of abundant date seed biomass and the simplicity of the hydrothermal–chemical activation process. The enhanced electrochemical performance is primarily associated with the hierarchical porous structure of the activated carbon and the improved ion transport facilitated by the hydrogel electrolyte, which collectively contribute to stable capacitive behavior and long-term cycling durability.