Ultrahigh vacuum and high-pressure coadsorption of CO and H2 on Pd(111): A combined SFG, TDS, and LEED study

Sum frequency generation (SFG) vibrational spectroscopy was carried out in conjunction with thermal desorption spectroscopy, low-energy electron diffraction, and Auger electron spectroscopy to examine the coadsorption of CO and H2 on Pd(111). Sequential dosing as well as various CO/H2 mixtures was utilized to study intermolecular interactions between CO and H2. Preadsorbed CO effectively prevented the dissociative adsorption of hydrogen for CO coverages ⩾0.33 ML. While preadsorbed hydrogen was able to hinder CO adsorption at low temperature (100 K), hydrogen was replaced from the surface by CO at 150 K. When 1:1 mixtures of CO/H2 were used at 100 K, hydrogen selectively hindered CO adsorption on on-top sites, while above ∼125 K no blocking of CO adsorption was observed. The observations are explained in terms of mutual site blocking, of a CO–H phase separation, and of a CO-assisted hydrogen dissolution in the Pd bulk. The temperature-dependent site blocking effect of hydrogen is attributed to the ability (inability) of surface hydrogen to diffuse into the Pd bulk above (below) ∼125 K. Nonlinear optical SFG spectroscopy allowed us to study these effects not only in ultrahigh vacuum but also in a high-pressure environment. Using an SFG-compatible ultrahigh vacuum-high-pressure cell, spectra of 1:10 CO/H2 mixtures were acquired up to 55 mbar and 550 K, with simultaneous gas chromatographic and mass spectrometric gas phase analysis. Under reaction conditions, CO coverages ⩾0.5 ML were observed which strongly limit H2 adsorption and thus may be partly responsible for the low CO hydrogenation rate. The high-pressure and high-temperature SFG spectra also showed indications of a reversible surface roughening or a highly dynamic (not perfectly ordered) CO adsorbate phase. Implications of the observed adsorbate structures on catalytic CO hydrogenation on supported Pd nanoparticles are discussed.