Temperature changes induced by 809‐nm GaAlAs laser at the implant–bone interface during simulated surface decontamination

The aim of the study was to investigate temperature changes at the implant-bone interface during simulated implant surface decontamination with a 809-nm gallium-aluminium-arsenid (GaAlAs) semiconductor laser. Stepped cylinder implants with a diameter of 3.8 mm and a length of 11 mm with two different surfaces (sand-blasted and acid etched, and hydroxyapatite-coated) were inserted into bone blocks cut from freshly resected pig femurs. Access holes of 0.5 mm were drilled into the bone, to allow K-type thermocouples to contact periimplant bone in different parts of the cavity. An artificial periimplant bone defect provided access for laser irradiation in the coronal third. A 600-micrometer optic fiber was used at a distance of 0.5 mm from the implant surface. Power output varied between 0.5 and 2.5 W in the continuous wave mode. The bone block was placed into a 37 degrees C water bath in order to simulate in vivo thermal conductivity and diffusitivity of heat. Temperature elevations during irradiation were registered for a period of 120 s. In mean, the critical threshold of 47 degrees C was exceeded after 9.0 s at 2.5 W, 12.5 s at 2.0 W, 18.0 s at 1.5 W and 30.5 s at 1.0 W. Surface characteristics did not have a significant effect on temperature elevations. In an energy-dependent manner, implant surface decontamination with an 809-nm GaAlAs laser must be limited in time to allow the implant and bone to cool down. Clinical guidelines are presented to avoid tissue damage.