ABSTRACT The anode in lithium–sulfur batteries (LSBs) is plagued by not only inhomogeneous lithium (Li) deposition, but also by parasitic side‐reactions. Often, a thick anode (∼400 µm) is used to compensate for these drawbacks, lowering gravimetric and volumetric energy densities. In this work, we demonstrate a ternary alloy anode fabricated via scalable thermal fusion of Li with aluminum (Al) and tellurium (Te) to cohesively address these issues. The Al–Li skeleton serves to homogenize Li deposition as well as reinforce the anode, allowing it to be rolled down to low thicknesses. Te incorporation suppresses the reaction of Li with polysulfides (Li 2 S n ) to form lithium sulfide (Li 2 S) and electrolyte degradation. It can also facilitate the formation of polytellurosulfides (Li 2 Te x Sy), which are far more conducive to Li + ‐ion diffusion. Even under a lean electrolyte/sulfur (E/S) ratio of 8 µL mg −1 and a low negative/positive (N/P) ratio of 3, capacities over 900 mA h g −1 at a C/5 rate are obtained in cells with Li–Te–Al anodes with a capacity retention of 80% after 70 cycles. In comparison, the baseline lithium‐metal anode retains only 35% after 50 cycles. Furthermore, the Li–Te–Al anodes confer a 24% boost to gravimetric energy density at the pouch cell level.
Shenoy et al. (Sun,) studied this question.