Microplastic contamination of low-density polyethylene mulch and nutrient loss from fertilizers present significant challenges in the crop-growing. In this study, the focus was on creating a biodegradable film that combines the advantages of plastic film , thermal insulation and water retention, as well as the controlled release of fertilizer. A key innovation was the efficient introduction of low molecular weight and low dispersibility of poplar lignin into chitosan and polyvinyl alcohol matrices. The lignin was extracted using deep eutectic solvents of binary carboxylic acids (choline chloride and maleic acid). The refined lignin was used as a superhydrophobic additive to improve the mechanical properties, hydrophobicity , and controlled nutrient release properties of the films through cross-linking. The mulch attained a tensile strength of 37.6 MPa, an elongation of 644.1 %, and a precise release of 53.1 % urea over 30 d at the ideal lignin content ratio (10 %). Furthermore, the film proficiently regulated soil temperature and moisture content . Successful enhancement of cabbage growth was achieved by actual measurements. This discovery provides innovative ideas for the development of nutrient slow-release high-strength integrated agricultural mulching films to promote sustainable, high-quality green agriculture . • A new deep eutectic solvent containing dicarboxylic acid groups was constructed. • Poplar lignin with low molecular weight and low polydispersity was extracted. • Lignin film with slow-release function was prepared by urea coating technology. • The mulch has excellent tensile strength , elongation and precise nutrient release.
Long et al. (Sun,) studied this question.