A facile approach of layer-by-layer depositing and hydrolysis of FeCl3 is developed to fabricate 3D-ordered Fe2O3 film. The 3D-ordered Fe2O3 film was characterized by SEM, XRD, and DRUV−vis. It has 3D-ordered interconnecting macropores (340 nm) with nanocrystalline hematite Fe2O3 walls (27.2 nm). The 3D-ordered macroporous nanocrystalline Fe2O3 film exhibits 2.4 times larger photocatalytic activity for the photodegradation of dye in the presence of H2O2 under visible irradiation than the nanocrystalline α-Fe2O3 film without macropores and very good photostability. The much higher photocatalytic activity of the 3D-ordered macroporous nanocrystalline Fe2O3 film than that of the reference Fe2O3 film is attributed to the unique nanostructure and architecture of the 3D-ordered Fe2O3 film, which result in the much greater light harvesting efficiency and efficient mass transport in the former than in the latter due to the existence of 3D-ordered interconnecting macropores. The effect of photonic stop band on the photocatalytic activity of the 3D-ordered Fe2O3 film was studied by angle-dependent solid-state photodegradation experiments with monochromatic irradiation. A slow photon enhancement of photocatalytic activity was achieved by adjusting the red edge of the photonic stop band of the 3D-ordered Fe2O3 film close to the electronic bandgap of Fe2O3. The photodegradation mechanism of crystal violet on the 3D-ordered Fe2O3 photocatalyst in the presence or absence of H2O2 was discussed.
No takes yet. Share an insight, caveat, or question.
Xie et al. (2010) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: