Explosive nucleation and growth of Pb islands on Ge(111) below room temperature via collective diffusion

Nucleation is a fundamental process in nature controlling phase transitions and pattern formation. Classical nucleation is based on the gradual aggregation of diffusing atoms after a critical cluster size is reached. Contrary to these expectations, we have observed in real time the formation of perfect Pb(111) islands with more than 10 5 atoms emerging out of the compressed wetting layer within a few seconds during growth of Pb on Ge(111) below room temperature. Pb deposited on Ge(111) in a temperature range between -30°C and 10°C exhibited explosive nucleation of height-selected islands upon reaching a critical coverage of 1.33±0.07ML with respect to Ge(111). Island nucleation was fueled by the 2% compression of the Pb wetting layer at the critical coverage. The island areas grew linearly with time, exhibiting collective diffusion, where thousands of atoms follow correlated, non-random walk diffusion. The total growth rate was higher with increasing temperature. Density functional theory simulations of the chemical potential and binding sites of the Pb/Ge(111) system give insight into the role of the compression of the wetting layer and the strain within the growing Pb layers, which explain this nonclassical behavior of the system.