Adhesion Enhancement and Performance Evolution of Waste Plastic Modified Asphalt with Liquid Anti-Stripping Agents

Waste plastics have attracted widespread attention in asphalt modification because of their environmental and economic benefits. However, the incorporation of waste plastics may weaken asphalt–aggregate interfacial adhesion, thereby increasing the risk of moisture damage in asphalt pavements. Although liquid anti-stripping agents have been widely used in conventional asphalt systems, their effectiveness and performance evolution in waste plastic-modified asphalt (WPA) remain insufficiently understood. To address this gap, this study systematically investigated the effects of two liquid anti-stripping agents, AJ-1 and AMR-II, on the adhesion, rheological properties, and aging behavior of WPA. Specifically, asphalt–aggregate adhesion was evaluated using water-boiling and binder bond strength tests, rheological properties were characterized by dynamic shear rheometer and bending beam rheometer tests, and aging behavior was analyzed through rolling thin-film oven test, pressurized aging vessel, and Fourier transform infrared spectroscopy. The results show that waste plastics reduce the adhesion performance at the asphalt-aggregate interface, whereas anti-stripping agents compensate for this loss. Compared with AJ-1, AMR-II showed stronger adhesion enhancement, increasing the asphalt residual coating ratio by approximately 1.5%–3.5% and the pull-off tensile strength by 17.4%–28.1%, while the corresponding improvements for AJ-1 were approximately 1.3%–2.7% and 13.0%–25.0%, respectively. As the dosage of both anti-stripping agents increased, the penetration index decreased, the temperature susceptibility increased, the softening point generally decreased, and the ductility increased markedly. Temperature sweep results show that both AJ-1 and AMR-II reduce the high-temperature performance of WPA. According to the bending beam rheometer results, AMR-II also enhances the low-temperature performance of WPA. Aging test results indicate that both anti-stripping agents increase the aging sensitivity of WPA to some extent, but the adverse effect of AMR-II on aging resistance is smaller than that of AJ-1, and AMR-II better preserves the low-temperature ductility and adhesion performance after aging. Overall, this study provides a binder scale evaluation showing that 0.4% AMR-II may offer a more balanced strategy for improving the adhesion and service performance of WPA.