Shannon Entropy of Corrected AE Data for Damage Assessment in CFRP-Strengthened RC Beams: From Brittle Shear to Distributed Failure

The abrupt failure of shear-deficient RC beams may lead to harmful consequences under dynamic loading. The use of Carbon Fiber Reinforced Polymers (CFRP) aims to convert this brittle fracture into a ductile one. However, the complexity of the multiple damage mechanisms makes it difficult to assess their condition using conventional testing methods. In this study, the damage evolution of a shear-critical reference beam and its CFRP-strengthened counterpart was monitored using the acoustic emission (AE) technique. After correcting attenuated AE amplitudes, damage analysis was performed using the Shannon entropy approach based on true source amplitudes. The entropy analysis performed with these corrected data clearly revealed the shear failure in the reference beam through abrupt drops in entropy, indicating damage homogenization. In contrast, the entropy remaining high and dynamically varying over a much longer deflection range in the CFRP-strengthened beam demonstrated that CFRP distributes damage over a wider region and that different damage mechanisms, such as debonding and fiber breakage, in addition to concrete cracking, were simultaneously active.