Transmission electron microscopy was used to study the ordered domain structures in undoped and La/Na‐doped Pb(Mg 1/3 Nb 2/3 )O 3 (PMN), where the compositions of the doped samples were specifically chosen so as to elucidate the ordering mechanism. The results showed that the Mg 2+ ions and Nb 5+ ions are short‐range ordered on the B‐site sublattice in undoped PMN, with a domain size of 2 to 5 nm. This short‐range ordering gives rise to B‐site composition fluctuations occurring on a nanometer scale, and it is this compositional inhomogeneity which is believed to be responsible for the diffuse phase transition behavior. Donor doping with La 2 O 3 can compensate for the local charge imbalance resulting from the short‐range order and thus enhances the degree of ordering. Acceptor doping with Na 2 O, however, increases the charge effect, and hence ordering is suppressed. The effect of Na doping and La doping on the dielectric properties of PMN is also discussed.