This study investigates the thermo-mechanical performance of fused filament fabrication (FFF)-printed polyphthalamide reinforced with 15 wt.% short carbon fibers (PPA CF15) for engineering applications under elevated temperature and cyclic loading conditions. The material was characterized by quasi-static tensile testing, fatigue testing, dynamic mechanical analysis (DMA), scanning electron microscopy (SEM), and finite element analysis (FEA). Tensile tests performed from 20 to 180 °C revealed a strong temperature-dependent reduction in mechanical properties: the elastic modulus decreased from 2.437 to 0.401 GPa, while the ultimate tensile strength decreased from 64.537 to 9.190 MPa. In contrast, elongation at break generally increased with temperature, indicating a transition toward more ductile deformation governed by thermal softening of the polymer matrix. Fatigue tests showed reduced fatigue resistance at higher temperatures and stress levels; however, stable cyclic performance was achieved when the applied stress remained below approximately 60–70% of the ultimate tensile strength, with several specimens reaching 106 cycles. DMA confirmed the viscoelastic nature of PPA CF15 and enabled the construction of frequency–temperature superposition master curves for numerical modelling. SEM observations revealed increased matrix deformation and fiber pull-out at elevated temperatures. FEA of an automotive intake manifold (IM) case study demonstrated that experimentally derived material data can be used to predict deformation, stress redistribution, and viscoelastic stabilization under combined thermal and mechanical loading. The results indicate that FFF-printed PPA CF15 is a promising lightweight composite for thermally and mechanically demanding automotive applications.
Ciganė et al. (Sun,) studied this question.