Optimizing Process Parameters for Plasma Nitriding of Super Duplex Stainless Steel in a Custom PIII System

This study aimed to optimize the nitriding parameters for Plasma Immersion Ion Implantation (PIII) of stainless steels. UNS S32750 super duplex stainless steel, widely employed in the petrochemical industry, was subjected to PIII under varying nitriding atmospheres (mixtures of H2 and N2) and treatment pressures. The fixed PIII nitriding parameters included a temperature of 300 °C, a duration of 3 h, a bias voltage of approximately −10 kV, a frequency of 500 Hz, and a pulse width of 30 μs. Following the treatments, the phases were characterized by X-ray diffraction (XRD), while the hardness and elastic modulus of the modified surfaces were evaluated via nanoindentation. Regarding the nitriding atmosphere, gas mixtures approaching a 60% N2/40% H2 (vol.) ratio yielded a higher volume fraction of nitrogen-rich expanded phases in solid solution. Furthermore, higher treatment pressures promoted the formation of these expanded phases, consequently enhancing the surface hardness up to 2.7 times the hardness value of the untreated sample. These findings stand in contrast to those found for low-energy plasma nitriding (PN) processes.