Halide solid electrolytes (SEs) are attracting great attention, owing to their high ionic conductivity and excellent high-voltage compatibility. However, severe moisture sensitivity, poor thermal stability, and instability at the lithium metal anode interface with chloride and bromide SEs retard their applications in solid-state lithium metal batteries. Fluoride SEs are expected to solve these problems, but they are now plagued by inadequate room-temperature (RT) ionic conductivity. Herein, a low-temperature molten salt (LiCl+1.33AlCl3) ablation method is proposed to enhance the ionic conductivity of monoclinic Li3GaF6 by particle boundary doping. The RT ionic conductivity of Li3GaF6 is correspondingly increased by 2 orders of magnitude, and the conductivity reaches 10–4 S cm–1 at 60 °C. The improved ionic conductivity benefits from the enhancement of interfacial ion transport, with the formation of more conductive chlorine-doped Li3GaF6–xClx and in situ binder LiAlCl4 to cement surrounding nanoparticles. The as-synthesized Li3GaF6 demonstrates outstanding humidity tolerance without conductivity degradation after exposure to a relative humidity of up to 35%. It also exhibits the widest electrochemical stability window experimentally (close to 6 V) compared with other state-of-the-art SEs. The solid-state Li/Li3GaF6/LiFePO4 cell with a stable Li+-conductive polymer interface is successfully driven for at least 200 cycles at 0.5C. Our study provides a solution to various chemical and electrochemical stability issues encountered by the halide SE family.
Nie et al. (Mon,) studied this question.