Experimental Investigation of Microstructural Evolution and Fatigue Damage of Pearlite Wheel Steel During Tread Braking Based on a Full-Size Wheel–Rail Test Rig

This study investigated the relationship between the surface microstructure of pearlite steel wheels and the formation of fatigue cracks during the braking process by using a full-size wheel braking test rig. After fatigue failure, the surface microstructural evolution and fatigue crack initiation and propagation of the wheel sample were systematically analyzed by optical microscope (OM), scanning electron microscope (SEM), and transmission electron microscope (TEM). The results showed that after braking of 1572 cycles, a large number of fatigue cracks formed at the wheel tread, which caused the wheel to break. After fatigue failure, some dark areas formed at the wheel tread, which were composed of Fe3O4 compounds. This indicates that severe oxidation was produced at the wheel tread during braking due to the high temperature. After fatigue failure, a continuous thermal white etching layer (T-WEL) was formed in some areas of the wheel tread, while crescent-shaped T-WEL was found in other areas. The microstructure of the T-WEL was composed of martensite phase. The rapid increase and decrease in temperature at the wheel tread during the braking process caused martensitic transformation at the wheel tread. The hardness of the sample reached to about 900 HV in WEL and it reduced with the increase in distance from the surface. The cracks were initiated from the surface and gradually propagated into the matrix. However, the crack propagation mode in the continuous T-WEL and crescent-shaped T-WEL was different. In the continuous T-WEL, the continuous T-WEL of the wheel can be peeled off during the braking wear process, and then the crack was gradually propagated into the matrix in the T-WEL peeled area. As for the crescent-shaped T-WEL, due to the large hardness difference between T-WEL and pearlite, the crack initiated at the interface between the T-WEL and pearlite and gradually propagated into the matrix.