Changes in Mechanical Properties and Structure of PET Films Treated with Metagenome-Derived LCCICCG PETase Heterologously Expressed in Penicillium verruculosum

This study examines the nature of enzymatic degradation of polyethylene terephthalate (PET) films mediated by a novel recombinant LCCICCG PETase enzyme preparation based on P. verruculosum fungus. The investigation was conducted using amorphous PET samples and PET samples with varying degrees of crystallinity as substrates for PETase-catalyzed hydrolysis under different temperature and pH conditions. Mechanical testing revealed that enzymatic treatment reduced the yield stress by 20–25%, tensile strength by approximately twofold, and elongation at break by 5–10 times, while the deformation mechanism remained unchanged. Enzymatic degradation under acidic conditions was ineffective, whereas increasing the pH to 9–10 markedly accelerated PET degradation and the associated deterioration of mechanical properties. Thermal analysis (TGA, DSC) and microscopy (optical and scanning electron microscopy) demonstrated that degradation was localized at the polymer surface, leading to the formation of cavities, cracks, and submicron-sized pores rather than bulk material disintegration. An inverse correlation was observed between PET crystallinity and susceptibility to enzymatic degradation: samples with crystallinity below 13% could be almost completely degraded, whereas samples with crystallinity above 30% exhibited little or no measurable weight loss over the same period. Low-crystallinity PET underwent rapid degradation accompanied by a transient increase in crystallinity, while highly crystalline PET primarily accumulated surface defects that nevertheless caused a substantial loss of mechanical strength. Consequently, the experimental data obtained in this study provide useful information for understanding PET degradation and for future studies on enzymatic PET recycling. The systematization of feedstock characteristics and the elucidated patterns of enzymatic degradation will enable optimization of pretreatment, enzymatic hydrolysis, and monomer recovery process parameters, thereby facilitating the eventual production of secondary raw materials.