Study on Persulfate Activation and Tetracycline Degradation by Chlorine-Doped Carbon Derived from ZIF-8

To address the inherent drawbacks of peroxymonosulfate advanced oxidation processes (PMS-AOPs), including the low efficiency of reactive species production, short radical half-lives, and restricted pollutant degradation performance, sodium salt-assisted modification was adopted to fabricate ZIF-8-derived carbon. In this study, sodium salt-assisted modification was adopted to treat ZIF-8, and the chlorine-doped derived carbon materials HNC-Tx-Cl were prepared for peroxymonosulfate activation and tetracycline degradation in water. Compared with NC-800 fabricated by direct calcination of ZIF-8 at 800 °C, HNC-800-Cl synthesized via NaCl-assisted calcination exhibits more abundant pore structures and richer carbon defects, with a specific surface area of 1115 m2/g and a high graphitic defect ratio ID/IG of 1.20. Catalytic tests reveal that HNC-800-Cl achieves 93.39% tetracycline removal within 90 min at a catalyst dosage of 0.05 g L−1 and PMS concentration of 0.1 mM. The system possesses a strong anti-interference ability toward complex water environments, maintaining a favorable degradation performance in the presence of coexisting anions, natural organic matter and actual water matrices. It also exhibits outstanding cycling stability, retaining a removal rate of 80.34% after five recycling runs. Radical quenching experiments and EPR characterization verify that superoxide radical (·O2−) is the dominant reactive species during tetracycline degradation. Both the radical and non-radical pathways are clarified to illustrate the mechanisms of PMS activation and pollutant degradation. This work provides a novel catalytic material strategy to overcome the deficiencies of conventional PMS-AOPs, and offers a new perspective for structural regulation and non-metallic doping modification of ZIF-8-derived carbon materials.