Flexible Intumescent Roll-Form Fire Protection for Enhancing the Fire Resistance Ratings of Building Structures

Intumescent coatings are widely used to enhance the fire resistance of structural steel. In contrast to traditional fire protection methods, this novel flexible intumescent protection offers several key advantages: universal compatibility with other coatings (via non-contact wrapping), resistance to extreme temperatures (−60 °C to +90 °C), all-weather usability, and suitability for light-gauge cold-formed thin-walled steel structures. This paper describes the development and investigation of these fire-protective, flexible intumescent coatings based on eco-friendly binders (silicone polymers and acrylic resins) with varying intercalated graphite (IG) content from 0% to 40%. An IG content of 25–40% enables a steel I-section with a section factor of 294 mm−1 to reach its limit state at 44 min (compared to 15 min for unprotected steel). Fire tests on steel beams with a section factor of 172 mm−1 demonstrated that samples reached the deflection limit state at the 64th and 66th minutes, respectively. Thermogravimetric analysis (TGA) was used to determine the temperature ranges for the thermal decomposition and expansion of the IG. Mechanical property studies revealed the influence of IG on the elastic modulus and tensile strength. Accelerated climatic testing in moderately cold conditions and salt spray chamber tests confirmed that the intumescent roll coating has no negative impact on the steel substrates.