The bimetallic catalyst has been one of the main categories of heterogeneous catalysts for chemical production and energy transformation. Isolation of the continuously packed bimetallic sites of a bimetallic catalyst forms singly dispersed bimetallic sites which have distinctly different chemical environment and electronic state and thus exhibit a different catalytic performance. Two types of catalysts consisting of singly dispersed bimetallic sites Pt 1 Co m or Pd 1 Co n ( m and n are the average coordination numbers of Co to a Pt or Pd atom) were prepared through a deposition or impregnation with a following controlled calcination and reduction to form Pt 1 Co m or Pd 1 Co n sites. These bimetallic sites are separately anchored on a nonmetallic support. Each site only consists of a few metal atoms. Single dispersions of these isolated bimetallic sites were identified with scanning transmission electron microscopy. Extended X-ray absorption fine structure spectroscopy (EXAFS) revealed the chemical bonding of single atom Pt 1 (or Pd 1 ) to Co atoms and thus confirmed the formation of bimetallic sites, Pt 1 Co m and Pd 1 Co n . Reduction of NO with H 2 was used as a probing reaction to test the catalytic performance on this type of catalyst. Selectivity in reducing nitric oxide to N 2 on Pt 1 Co m at 150 °C is 98%. Pd 1 Co n is active for reduction of NO with a selectivity of 98% at 250 °C. In situ studies of surface chemistry with ambient-pressure X-ray photoelectron spectroscopy and coordination environment of Pt and Pd atoms with EXAFS showed that chemical state and coordination environment of Pt 1 Co m and Pd 1 Co n remain during catalysis up to 250 and 300 °C, respectively. The correlation of surface chemistries and structures of these catalysts with their corresponding catalytic activities and selectivities suggests a method to develop new bimetallic catalysts and a new type of single site catalysts.
Nguyen et al. (Thu,) studied this question.