Multishelled Ni‐Rich Li(NixCoyMnz)O2 Hollow Fibers with Low Cation Mixing as High‐Performance Cathode Materials for Li‐Ion Batteries

A simple seaweed biomass conversion strategy is proposed to synthesize highly porous multishelled Ni-rich Li(NixCoyMnz)O2 hollow fibers with very low cation mixing. The low cation mixing results from the cation confinement by the novel “egg-box” structure in the alginate template. These hollow fibers exhibit remarkable energy density, high-rate capacity, and long-term cycling stability when used as cathode material for Li-ion batteries. Layered Li(NixCoyMnz)O2 is one of the most promising cathode materials for lithium ion batteries (LIBs), due to its stable structure, compositional flexibility, thermal stability, low cost, and relatively high reversible capacity.1, 2 In particular, the Ni-rich oxides such as Li(NixCoyMnz)O2 (x ≥ 0.5) have attracted intense research attention,3 since they provide very high specific capacity, ≈212 mAh g−1 for x = 0.8 and 220 mAh g−1 for x = 0.86. However, unlike low Ni content oxides which generally exhibit outstanding stabilities,2 Ni-rich oxides suffer inherent drawbacks including poor cycle life and rate performance due to low Li diffusion rates caused by cation mixing. This manifests as Ni2+ ions occupying 3b Li sites in the Li slab, whilst Li+ ions also occupy sites in the transition metal (TM) layers. This cation mixing leads to a higher activation energy barrier for Li diffusion because of the smaller separations between the TM layers, and also leads to structural instability during electrochemical charge/discharge cycles.4 Many approaches have been adopted to address the cation mixing and disorder in Ni-rich materials. Most approaches focus on adjusting the synthesis conditions to reduce cation migration from the TM site to Li site by controlling the lithiation temperature5 or the Li/TM ratio.6 However, in these methods, an excess of Li is necessary to produce highly ordered Ni-rich oxides. Residual Li remains on the surface of the active materials and reacts with air to form LiOH and Li2CO3, leading to undesirable side reactions with the electrolyte. The undesirable LiOH and Li2CO3 species also impede the diffusion of Li+ ions due to their insulating properties, and thus deteriorate the electrochemical cycle performance.5 In addition, traditional synthesis methods, which usually involve coprecipitation and annealing at high temperature, do not allow controllable synthesis of Ni-rich nanostructures needed to address the sluggish Li+ ion diffusion.6, 7 Therefore, excellent rate performance and high specific capacity are hard to achieve. Structure can strongly influence the functionality of electrode materials. To avoid cation mixing and thus improve the performance of Ni-rich Li(NixCoyMnz)O2 electrodes, the design of 1D structures is a prudent strategy. 1D structures also guarantee a high electrode–electrolyte contact area and a short transport path for electrons and Li+ ions,8 all of which could be expected to improve the rate performance of the Li(NixCoyMnz)O2 materials. In addition, porous electrodes with multishelled structures have attracted interest in recent years based on the following advantages.9 First, porous multishelled structures offer more channels for Li+ ions and thus are helpful for enhancing the specific capacity. Second, the multishelled structures have a very short path for Li+ ion diffusion, leading to good rate performance. Thus, it is easily envisaged that a multishelled Ni-rich Li(NixCoyMnz)O2 hollow fiber (HF), combining the advantages of a 1D morphology and a porous multishelled structure, should exhibit high-performance as cathode materials for LIBs. In this Communication, we report the synthesis of a series of multishelled Ni-rich Li(NixCoyMnz)O2 (x = 0.8, 0.7, 0.65, and 0.5) HFs with low cation mixing using sustainable seaweed (alginate) fiber as template. The Mn+(M = Ni, Co, Mn) cations were first immobilized into a novel “egg-box” arrangement via coordination with negatively charged α-l-guluronate (G) blocks of the linear alginate macromolecule.10 Meanwhile, the β-d-mannuronate (M) blocks in alginate can absorb Li+ via the negatively charged carboxyl groups.11 This approach suppresses cation mixing or the formation of undesirable LiOH and LixCO3 species in subsequent calcination step used to synthesize the HFs. The Li-M alginate fibers (Li-M-AFs) were converted to multishelled HFs by calcination. The combustion of the alginate precursor introduces high porosity in the fibers. As expected, the 1D multishelled Li(NixCoyMnz)O2 HFs demonstrate superior discharge capacity of 219.9 mAh g−1 at 0.5 C (x = 0.8) compared with conventional Li(NixCoyMnz)O2 materials, and an outstanding capacity retention of 84.36% after 300 cycles. The synthesis of the multishelled Ni-rich Li(NixCoyMnz)O2 HFs is described in Scheme 1a. Calcium alginate microfibers (Ca-AFs) were prepared from aqueous sodium alginate using a wet-spinning method (see Synthesis of multi-shelled Li(NixCoyMnz)O2 hollow fiber, Supporting Information), and used as templates. The obtained Ca-AFs were then transformed into protonated alginate fibers (H-AFs) by immersion in a 1 m HCl aqueous, resulting in complete Ca2+/H+ exchange. The protonated alginate was then soaked in a mixed aqueous solution of cobalt acetate, nickel acetate, and manganese acetate to form purple M-alginate fibers (M-AFs). This immobilized the Mn+ cations (M = Ni, Co, Mn, respectively) into an “egg-box” arrangement through coordination by the four G-block of alginate.12, 13 The molar ratio of Ni/Co/Mn in the M-AFs can be easily controlled by adjusting the ratio of the three cations in the aqueous solution. Herein, four different M-AFs were prepared with precisely controlled Ni/Co/Mn molar ratios (see Table S1, Supporting Information). The M-AFs were then dispersed in a suspension of Li2CO3 in H2O:EtOH (1:2) for 0.5 h to obtain the Li-M-AFs, in which the Li+ was immobilized electrostatically by the alginate carboxyl groups. Calcination of the Li-M-AFs at different temperatures yielded multishelled Li(NixCoyMnz)O2 HFs (x = 0.8, 0.7, 0.65, and 0.5). The morphology and structure of Li(NixCoyMnz)O2 HFs were characterized by field emission scanning electron microscopy (FESEM). As shown in Figure 1, the five Li(NixCoyMnz)O2 samples exhibit a 1D fibrous morphology. The diameter of these fibers is ≈10 μm, which is approximately one half that of the Ca-AFs (see Figure S1, Supporting Information, ≈20 μm) and the ion-exchanged Li-M-AFs (see Figure S2, Supporting Information, ≈20 μm). The shrinkage of the fibers during the calcination step can mainly be attributed to combustion of the alginate network in the fibers. Interestingly, the cross-section images of the fibers reveal a novel multishelled hollow structure (see Figure 1a–d). Most of the fibers are highly porous with double or triple shells (see Figure S3, Supporting Information), with the thickness of the individual shells reaching several hundred nanometers. The multishelled morphology with wide space between the shells is highly desirable, as it is expected to effectively increase the electrode/electrolyte contact area and enhance the diffusion rates for both Li+ ions and electrons. Elemental mapping by energy dispersive X-ray spectroscopy (EDS) was used to analyze the composition of Li(Ni0.65Co0.25Mn0.1)O2 HFs. As shown in Figure 1e, Ni, Co, and Mn are homogeneously distributed over a single fiber. The results from the EDS analysis (see Figure 1f) reveal that the molar ratios of Ni, Co, and Mn in the fibers were in excellent accord with the nominal values of 0.65:0.25:0.1. The accurate chemical composition of the fibers was determined using inductive coupled plasma atomic emission spectrometry (ICP-AES). Excellent agreement was found between the nominal and actual molar ratios of Li, Ni, Co, Mn in the Li(NixCoyMnz)O2 HFs (see Table S2, Supporting Information). The information above allows the multishelled structure of the Li(NixCoyMnz)O2 HFs to be rationalized, as illustrated in Scheme 1b. In the initial stage of the calcination process, the long-chain Mn+-alginate molecules partially migrate toward the surface of the fibers, whilst the inner solid core contracts to form a core–shell structure due to nonequilibrium heat transfer. With heating to higher temperatures, the migration of Mn+-alginate molecules and inner core contraction reoccurs, along with combustion of the alginate template resulting in the formation of the porous multishelled Li(NixCoyMnz)O2 HFs. FESEM images of Li-M-AFs heated from 250 to 750 °C successfully document the evolution of the porous multishelled hollow structure (see Figure S4, Supporting Information). The first shell appears at temperature around 450 °C, and the porous network and the second shell appear around 550 °C. Complete combustion of alginate-derived carbonaceous component yields Li(NixCoyMnz)O2 shells. The carbon combustion creates voids in the shells, and thus the multishelled HFs are highly porous. The space between the shells ensures excellent electrode–electrolyte contact, whilst the porous network in the shells provides a short pathway for electron and Li+ diffusion, both of which could be expected to significantly improve the rate performance and the specific capacity of Li(NixCoyMnz)O2. Powder X-ray diffraction (XRD) patterns for all the Li(NixCoyMnz)O2 HFs are shown in Figure S5 of the Supporting Information. The (006)/(102) and (108)/(110) doublets indicate that all Li(NixCoyMnz)O2 HFs possess a well-defined layered structure based on a hexagonal a-NaFeO2 structure with a Rspace group.14 The ratio I(003)/I(104) reflects the degree of cation mixing caused by occupation of Li+ sites by Ni2+, which occurs due to the similar ionic radii of Ni2+(0.069 nm) and Li+(0.076 nm).15 Cation mixing seriously weakens cycle life and rate performance of Li(NixCoyMnz)O2 materials. As shown in Table S3 of the Supporting Information, the ratio of I(003)/I(104) for the Ni-rich HFs ranges from 1.31 for x = 0.5 to 1.24 for x = 0.8. Given that the cation mixing is considered negligible if the ratio I(003)/I(104) is higher than 1.20,16 it can be concluded that the Ni-rich Li(NixCoyMnz)O2 HFs synthesized here exhibit an unusually low degree of cation mixing. To probe Li+/Ni2+ ion disorder in detail, we refined the XRD patterns based on the Rietveld method using General Structure Analysis System (GSAS) software (Figure 2a). The initial occupation parameters of all atoms are based on formula (Li1Ni2)3b(Li2NiCo1Mn1)3aO2, in which Li1/Ni2are set at 3b site, Li2/Ni1/Co1/Mn1 at 3a site, and O at 6c site. The occupation parameters of Co and Mn at the 3a site are fixed, and the total amount of Li and Ni within the materials fixed, while the distribution of Li and Ni between the 3a and 3b sites is variable. According to the calculated occupation parameters, the crystallographic formulas for the multishelled Li(NixCoyMnz)O2 hollow fibers (x = 0.8, 0.7, 0.65, and 0.5) are (Li0.9352Ni0.0675)3b(Li0.0675Ni0.7325Co0.1Mn0.1)3aO2, (Li0.9338Ni0.0662)3b(Li0.0662Ni0.6338Co0.20Mn0.1)3aO2, (Li0.9472Ni0.0528)3b(Li0.0528Ni0.5972Co0.25Mn0.1)3aO2, and (Li0.9515Ni0.0485)3b(Li0.0485Ni0.4515Co0.2Mn0.3)3aO2, respectively. These models provided an excellent fit to the experimental XRD data, as can be seen in Figure 2b–e. With an increase in the Ni content from x = 0.5 to 0.8, the Li/Ni exchange increases from 0.0485 to 0.0675, though the latter value is still significantly lower than the value of 0.085 reported for bulk Li(Ni0.65Co0.25Mn0.1)O2 with x = 0.7.2 The XRD patterns of the Li(Ni0.65Co0.25Mn0.1)O2 precursor calcined at temperatures from 150 to 750 °C are shown in Figure S6 of the Supporting Information. Crystalline Li(Ni0.65Co0.25Mn0.1)O2 appears when the annealing temperature is higher than 350 °C. The ratio I(003)/I(104) is higher than 1.26 at calcination temperatures above 350 °C (see Table S4, Supporting Information). At lower temperatures, the M2+ ions are confined into the “egg-box” and cannot migrate freely to Li+ sites (see Scheme 1a). At high temperatures, the “egg-box” converts to carbon/metal core/shell structure,10-12 with the carbon shell preventing cation mixing until it is completely consumed by combustion. Obviously, the use of the Li-M-AF precursor plays a key role in minimizing cation disorder during the calcination step used in the synthesis of the Li(Ni0.65Co0.25Mn0.1)O2 HFs. X-ray photoelectron spectroscopy (XPS) examines the valence states of Li, Ni, Co, Mn, and O in the Li(NixCoyMnz)O2 HFs. Li 1s, Ni 2p, Co 2p, Mn 2p, and O 1s XPS spectra for Li(Ni0.65Co0.25Mn0.1)O2, which exhibits the best cycle performance in the electrochemical tests, are displayed in Figure 2. The corresponding XPS survey spectrum is shown in Figure S7a of the Supporting Information. The spectra presented here for Li(Ni0.65Co0.25Mn0.1)O2 are representative of all the Li(NixCoyMnz)O2 HFs synthesized in this work. The C 1s peak is due to the residual hydrocarbon on the sample surface during the synthesis process. Deconvolution of Li 1s in Figure 2f gives the peak with binding energies of 56.9 eV, which is in good agreement with the results reported in lithium oxide cathode materials.17 The Ni 2p3/2 peak at 854.2 eV and associated satellite feature at 861.2 eV are characteristic for a Ni(II) oxide species (Figure 2g).18 The Ni 2p3/2 peak at 855.8 eV indicates the coexistence of Ni(III).19 The Co2p3/2 region contained two peaks (Figure 2h), a main peak at 779.0 eV and the weaker peak at 780.4 eV which are assigned to tri- and divalent Co species,1, 20 respectively. The Mn 2p3/2 peak was deconvoluted into two signals at 641.7 and 642.5 eV, which are assigned to Mn(III) and Mn(IV) species, respectively.1 The O1s spectrum (Figure S7b, Supporting Information) contains three signals peaks at 526.6, 528.9, and 530.3 eV, assigned to coordinated oxygen, lattice oxygen, and coordinatively unsaturated surface oxygen,21 respectively. Surface carbonate may also contribute to the O 1s spectrum, since a C 1s signal was seen in the survey spectrum and assigned to a carbonate species. In any case, the XPS results are in good agreement with the previously reported Ni-rich (x = 0.65) Li(NixCoyMnz)O2 materials.19 Representative transmission electron microscopy (TEM) and high-resolution TEM (HRTEM) images of Li(Ni0.65Co0.25Mn0.1)O2 HFs are shown in Figure 3. Figure 3a shows a fragment of the porous HF shell, and is composed of nanoparticles with a mean size of ≈120 nm. The corresponding selected area electron diffraction (SAED) pattern (Figure 3b) reveals the shell is polycrystalline. Figure 3c shows a single-crystal SAED pattern taken from one of the nanoparticles, which can be indexed to hexagonal Li(Ni0.65Co0.25Mn0.1)O2 projected alone its 100 zone axis. A HRTEM image was taken from the nanoparticle facet boxed in Figure 3a, and is shown in Figure 3b. The HRTEM image shows d-spacings of 0.23 and 0.47 nm, corresponding to (012) and (003) lattice fringes of hexagonal Li(Ni0.65Co0.25Mn0.1)O2 (space group R, a = b = 0.2873, and c = 1.4273 nm). The corresponding fast Fourier transform (FFT) pattern (inset in Figure 1d) is equivalent to the SAED pattern of the whole particle. To evaluate the potential of the multishelled Li(NixCoyMnz)O2 HFs as the cathode materials for LIBs, their electrochemical properties were examined by cyclic voltammetry (CV) and galvanostatic cycling techniques. The initial charge/discharge curves, obtained from cells containing multishelled Li(NixCoyMnz)O2 HFs (x = 0.8, 0.7, 0.65, and 0.5) cycling between 2.5 and 4.5 V at a rate of 20 mA g−1 at 25 °C, are presented in Figure 4a. The initial discharge capacity of the electrodes increased with increasing Ni content (x), which can likely be attributed to the lower diffusion energy barriers to delithiation of Ni-sites.22 The discharge capacities are 229.9, 217.2, 211.5, and 204.4 mAh g−1 for x = 0.8, 0.7, 0.65, and 0.5, respectively. These values are among the best yet reported Li(NixCoyMnz)O2 cathodes. The gap between the theoretical (≈275 mAh g−1) and observed capacities is ascribed to irreversible reactions, such as the decomposition of the electrolyte.23 CVs for all electrode materials are shown in Figure S8, Supporting Information. The Li(NixCoyMnz)O2 samples show peaks at 3.76 V on charging and 3.72 V on discharging. A further higher charging potential peak at about 4.2 V is seen for cells containing Ni-rich Li/Li(NixCoyMnz)O2 HFs (x = 0.8 and 0.7). The two delithiation stages at 3.76 V and 4.2 V likely correspond to the oxidation of Ni2+ to Ni3+ and Ni3+ to Ni4+, respectively, in such Ni-rich samples.22, 24 Figure 4b compares the cycling performance of the multishelled Li(NixCoyMnz)O2 HFs. After 200 deep discharge/charge cycles between 2.5–4.5 V at 0.5 C, the samples still retain discharge capacities of 200.4, 197.0, 193.1, and 190.5 mAh g−1, for x = 0.8, 0.7, 0.65 and 0.5, respectively. Capacity retentions are therefore 91.21%, 91.85%, 92.20%, and 94.20%, respectively. After 300 electrochemical cycles, the capacity retention was 84.36% for x = 0.8. This performance level is far superior to most Ni-rich electrodes reported (Figure 4e).1, 2, 25 Even when the Li/Li(NixCoyMnz)O2 cells were tested at a high cut-off potential of 4.6 V versus Li/Li+ for 100 cycles (Figure S9, Supporting Information), the capacity retention for the electrode with x = 0.5 was still 91.40%, much higher than the best previously reported value of 85%.12 Clearly, the multishelled hollow fibrous electrodes exhibit outstanding cycling stability, compared with the convention Ni-rich Li(NixCoyMnz)O2 electrodes.14 Extended cycling stability measurements were conducted at different current densities. As shown in Figure 4c, all the Ni-rich Li(NixCoyMnz)O2 electrodes exhibit excellent rate capability on increasing the current density stepwise from 0.1 to 10 C. Example, as the current density was increased stepwise from 0.1 to 0.2, 0.5, 1, 2, 5, and 10 C, the Li(Ni0.8Co0.1Mn0.1)O2 electrode delivered stable capacities of 229.6, 225.5, 216.7, 207.4, 196.6, 183.4, and 172.7 mAh g−1, respectively. More importantly, when the current density was returned back to 0.1 C, full capacities were recovered for all the multishelled hollow electrodes, indicating their excellent rate performance. Figure 4d displays impedance spectra for the multishelled Li(NixCoyMnz)O2 hollow fibrous electrodes after 5 cycles. The impedance parameters are fitted by the same equivalent circuit (see inset in Figure 4d). The impedance parameters are fitted by the same equivalent circuit shown as the inset in Figure 4d. The high-frequency intercept at the is the of the and The is the of the solid and the at the between the and the The the impedance which to the Li+ ion diffusion in the electrode materials. At the same the value was found for the Li(Ni0.8Co0.1Mn0.1)O2 indicating that sample the to and the sample the discharge capacity the four HF samples was in to the Ni content in the which can be in of the higher delithiation barriers of and in with Figure 5 the advantages of the multishelled Li(NixCoyMnz)O2 HFs during electrochemical First, the 1D morphology of the fiber shells allows fast Li+ and which is for electrochemical performance. Second, the space between the shells can the by as by the diffusion of Li+ and the porous network on the shell to reduce the electron and Li+ ion diffusion and also electrons from all to the Li(NixCoyMnz)O2 which is highly for the specific The of all these to the remarkable of the multishelled Ni-rich Li(NixCoyMnz)O2 HFs. In to the fast Li+ diffusion in the multishelled Ni-rich Li(NixCoyMnz)O2 the Li+ ion diffusion was determined via (Figure Supporting Information). As the Ni content the Li+ ion diffusion since the delithiation barrier is lower compared to that of or Figure of the Supporting also compares the Li+ ion diffusion of μm, Figure Supporting Information) and multishelled HFs. The Li+ ion diffusion for multishelled HF for much higher than the determined for The Li+ ion diffusion of and multishelled HF were also by using galvanostatic are shown in Figure and Figure and of the Supporting Information, respectively. Figure of the Supporting shows the calculated diffusion at different of = 0.2, and the multishelled HF and show the same with the increase of value from to the stage of the Li space to Li+ ion diffusion due to the of the slab, and the valence of Ni from Ni2+ to Ni3+ and Ni4+, which leads to the increase of diffusion by diffusion = 0.5, the Li+ diffusion of multishelled HF is which is much than that of Figure Supporting Information). In a series of multishelled or Ni-rich Li(NixCoyMnz)O2 HFs were successfully synthesized by using a sustainable biomass as a template. The novel structure of the alginate effectively Ni2+, and which suppresses cation mixing during a subsequent calcination step used in the synthesis of the Li(NixCoyMnz)O2 HFs. These HF cathode materials exhibit much higher specific capacity, cycling performance and rate capability compared with all Ni-rich Li(NixCoyMnz)O2 reported to The very low cation mixing and structure such as 1D morphology and porous multishelled hollow structure contribute to the outstanding electrochemical performance. This the potential of multishelled Ni-rich Li(NixCoyMnz)O2 HFs as cathode materials for lithium ion and to this work. the from the of and of the of and of in for As a to and this provides information by the materials are and may be for are not or from information than should be to the The is not for the content or functionality of any information by the than should be to the corresponding for the