To advance sustainable packaging development, this study investigates modifying pectin-based films with citric acid cross-linking and nanocellulose reinforcement to enhance their functional properties. Cross-linked citrus pectin (CLCP) films were obtained from film-forming solutions containing different amounts of pectin (2.5–3.5 g 100 mL −1 ) and citric acid (1–2 g 100 mL −1 ), with glycerol (1–3 mL 100 mL −1 ), and nanocellulose (0–2 g 100 mL −1 ) added as a plasticizer and reinforcing agent, respectively. CLCP films were comprehensively characterized concerning structural, mechanical, and barrier properties. FTIR confirmed successful cross-linking, whereas the structural modifications occurred in the pectin network after cross-linking were elucidated for the first time using advanced 2D-NMR. Principal component analysis (PCA) revealed that nanocellulose concentration was the most significant factor in improving mechanical properties, with strong positive correlations with tensile strength ( r = 0.586) and Young's modulus ( r = 0.639). Conversely, glycerol concentration showed the strongest negative correlation ( r = −0.746 and −0.741, respectively), confirming its plasticizing effect. Barrier properties were also significantly influenced: higher citric acid concentration and processing temperature improved the oxygen barrier. In contrast, higher pectin and nanocellulose concentrations decreased the oxygen transmission rate ( r = −0.636 and r = −0.733, respectively). This systematic analysis provides a comprehensive design map for tuning film properties, demonstrating that co-modifying pectin with citric acid and nanocellulose is a highly effective strategy for developing advanced, sustainable packaging materials with tailored performance.
Chandrasekar et al. (Fri,) studied this question.