This paper describes the magnetic properties of NiZnCu ferrite film deposited at room temperature by an aerosol deposition method (ADM). The thickness of the film was 6 μm and the deposition rate was estimated as 2 μm/min. The microstructure of as‐deposited at room temperature films consists of randomly oriented nanocrystallites with a size of 20 nm. As‐deposited and annealed films exhibited the following magnetic properties: intensity of magnetization M s = 0.147 T (117 emu/cm 3 ), coercivity H c = 40.58 kA/m (510 Oe); and M s = 0.3 T (250 emu/cm 3 ), H c = 14.95 kA/m (188 Oe), respectively.