Epitaxial growth of A–A and A–B stacking MoS2 on WS2 via a two-step chemical vapor deposition method is reported. These epitaxial heterostructures show an atomic clean interface and a strong interlayer coupling, as evidenced by systematic characterization. Low-frequency Raman breathing and shear modes are observed in commensurate stacking bilayers for the first time; these can serve as persuasive fingerprints for interfacial quality and stacking configurations. As a service to our authors and readers, this journal provides supporting information supplied by the authors. Such materials are peer reviewed and may be re-organized for online delivery, but are not copy-edited or typeset. Technical support issues arising from supporting information (other than missing files) should be addressed to the authors. Please note: The publisher is not responsible for the content or functionality of any supporting information supplied by the authors. Any queries (other than missing content) should be directed to the corresponding author for the article.
Zhang et al. (Mon,) studied this question.