Abstract Fluorescent nanodiamonds (FNDs) containing negatively charged nitrogen-vacancy (NV − ) centers are vital for many emerging quantum sensing applications from magnetometry to intracellular sensing in biology. However, developing a scalable fabrication method for FNDs hosting color centers with consistent bulk-like photoluminescence (PL) and spin coherence properties remains a highly desired but unrealized goal. Here, we investigate optimized ball milling of single-crystal diamonds produced via chemical vapor deposition (CVD) and containing 2 ppm of substitutional nitrogen and 0.3 ppm of NV − to achieve this goal. The NV charge state, PL lifetime, and spin properties of bulk CVD diamond samples are directly compared to milled CVD FNDs and commercial high-pressure high-temperature (HPHT) FNDs. We find that on average, the relative contribution of the NV − charge state to the total NV PL is lower and the NV PL lifetime is longer in CVD FNDs compared to HPHT FNDs, both likely due to the lower N s 0 concentration in CVD FNDs. The CVD bulk and CVD FNDs on average show similar average T 1 spin relaxation times of 3.2 ± 0.7 ms and 4.7 ± 1.6 ms, respectively, compared to 0.17 ± 0.01 ms for commercial HPHT FNDs. Our results demonstrate that ball milling of CVD diamonds enables the large-scale fabrication of NV ensembles in FNDs with bulk-like T 1 spin relaxation properties.
Mameli et al. (Thu,) studied this question.