To improve the utilization of visible light and reduce photogenerated electron/hole recombination, Ti 3+ self-doped TiO 2 /oxygen-doped graphitic carbon nitride (Ti 3+ -TiO 2 /O-g-C 3 N 4 ) heterojunctions were prepared via hydrothermal treatment of a mixture of g-C 3 N 4 and titanium oxohydride sol obtained from the reaction of TiH 2 with H 2 O 2 . In this way, exfoliated O-g-C 3 N 4 and Ti 3+ -TiO 2 nanoparticles were obtained. Simultaneously, strong bonding was formed between Ti 3+ -TiO 2 nanoparticles and exfoliated O-g-C 3 N 4 during the hydrothermal process. Charge transfer and recombination processes were characterized by transient photocurrent responses, electrochemical impedance test, and photoluminescence spectroscopy. The photocatalytic performances were investigated through rhodamine B degradation test under an irradiation source based on 30 W cold visible-light-emitting diode. The highest visible-light photoelectrochemical and photocatalytic activities were observed from the heterojunction with 1:2 mass ratio of Ti 3+ -TiO 2 to O-g-C 3 N 4 . The photodegradation reaction rate constant based on this heterojuction is 0.0356 min –1, which is 3.87 and 4.56 times higher than those of pristine Ti 3+ -TiO 2 and pure g-C 3 N 4, respectively. The remarkably high photoelectrochemical and photocatalytic performances of the heterojunctions are mainly attributed to the synergetic effect of efficient photogenerated electron–hole separation, decreased electron transfer resistance from interfacial chemical hydroxy residue bonds, and oxidizing groups originating from Ti 3+ -TiO 2 and O-g-C 3 N 4 .
Li et al. (Tue,) studied this question.