Poly(thieno[3,2-b]thiophene-alt-bithiazole): A D–A Copolymer Donor Showing Improved Photovoltaic Performance with Indene-C₆₀ Bisadduct Acceptor

A new D–A copolymer, poly(thieno[3,2- b ]thiophene- alt -bithiazole) ( PTTBTz ), based on thieno[3,2- b ]thiophene donor unit and bithiazole acceptor unit, was synthesized by the Pd-catalyzed Stille-coupling reaction for the application as donor material in polymer solar cells (PSCs). PTTBTz film possesses high thermal stability with 5% weight-loss temperature at 450 °C, a lower-lying HOMO energy level at −5.20 eV, a higher hole mobility of 6.45 × 10 –3 cm 2 /(V s), and a crystalline structure. Photovoltaic performance of the polymer was investigated with [6,6]-phenyl-C 71 -butyric acid methyl ester (PC 70 BM) or indene-C 60 bisadduct (ICBA) as acceptor and with 3% DIO additive. The power conversion efficiency (PCE) of the PSC based on PTTBTz:ICBA (1:1 w/w) reached 5.35% with a high V oc of 1.03 V, a J sc of 8.55 mA/cm 2, and an FF of 0.608, whereas the PCE of the PSC based on PTTBTz:PC 70 BM (1:1 w/w) was 4.57% with a V oc of 0.82 V, a J sc of 9.89 mA/cm 2, and an FF of 0.563, under the illumination of AM1.5, 100 mW/cm 2 . PTTBTz is one of the D–A copolymers that shows better photovoltaic performance with ICBA as acceptor than PC 70 BM. PTTBTz /ICBA could be a promising front active layer for high-efficiency tandem PSC because of its high V oc .