Experimental investigation and correlation of viscosity for MgO–MWCNT–CeO2/water hybrid nanofluid

This study is focused on the viscosity of mono-nanofluids (MNFs) composed of CeO 2 /water, MWCNT/water, and MgO/water, as well as hybrid nanofluids (HNFs) namely MgO-MWCNT/water, MgO-CeO 2 /water, and CeO 2 -MWCNT/water. Additionally, a ternary hybrid nanofluid (THNF) of MgO-CeO 2 -MWCNT/water was examined. The study encompassed temperatures ranging from 20 to 60 ℃ and solid volume fractions (SVFs) of 0.1% and 0.3% for MNFs and HNFs, while THNF was studied at SVFs of 0.1%, 0.2%, 0.3%, 0.4%, and 0.5%. Post-nanofluid preparation, zeta potential and dynamic light scattering (DLS) tests were performed to confirm stability, with tests conducted at the highest SVF (SVF = 0.5%), indicating favorable nanofluid quality. Brookfield viscometer measurements were employed to assess nanofluid viscosity. The experimental findings revealed that viscosity decreases with rising temperature at a constant SVF, while it increases with rising SVF at a constant temperature. Notably, at SVF = 0.1% and 0.3%, the most significant viscosity increase occurred in the water/MWCNT MNF, reaching 2.7 times that of the base fluid (BF) at SVF = 0.3% and T = 40 ℃. For THNF, the highest viscosity increase was observed at SVF = 0.5% and T = 50 ℃, growing approximately 1.3 times that of BF. Subsequently, a mathematical model was proposed to predict THNF viscosity, demonstrating high consistency with laboratory results.