Preparation and Characterization of Te/Poly(3,4-ethylenedioxythiophene):Poly(styrenesulfonate)/Cu₇Te₄ Ternary Composite Films for Flexible Thermoelectric Power Generator

In this work, Te/poly(3,4-ethylenedioxythiophene) (PEDOT):poly(styrenesulfonate) (PSS)/Cu 7 Te 4 ternary thermoelectric (TE) nanocomposite films were successfully fabricated by physical mixing and then drop casting. An optimum power factor of 65.3 μW/mK 2 was acquired from a composite film containing 95 wt % PEDOT:PSS-coated Te (PC/Te) nanorods at 300 K, which was about 5 times as large as that of the PC/Cu 7 Te 4 nanorod film and about 3 times as large as that of the PC/Te nanorod film. The power factor reached 112.3 μW/mK 2 when the temperature was 380 K. Scanning transmission electron microscopy (STEM) and high-resolution STEM were used to observe the detailed internal microstructure of the composite film, revealing that the Te nanorods were single crystalline and the Cu 7 Te 4 rods polycrystalline. The composite film was in fact a three-dimensional network interconnected with the PC/Te and PC/Cu 7 Te 4 nanorods. The enhancement of the TE properties was ascribed to the synergetic effect of the two kinds of nanorods and the double-carrier filtering effect at the two heterointerfaces of Te/PEDOT:PSS and Cu 7 Te 4 /PEDOT:PSS. An eight single-leg flexible TE device consisting of the optimized composite film was fabricated, which produced a voltage of 31.2 mV and a maximum output power of 94.7 nW at a temperature gradient of 39 K.