Side-Chain-Induced Rigid Backbone Organization of Polymer Semiconductors through Semifluoroalkyl Side Chains

While high-mobility p-type conjugated polymers have been widely reported, high-mobility n-type conjugated polymers are still rare. In the present work, we designed semifluorinated alkyl side chains and introduced them into naphthalene diimide-based polymers (PNDIF-T2 and PNDIF-TVT). We found that the strong self-organization of these side chains induced a high degree of order in the attached polymer backbones by forming a superstructure composed of "backbone crystals" and "side-chain crystals". This phenomenon was shown to greatly enhance the ordering along the backbone direction, and the resulting polymers thus exhibited unipolar n-channel transport in field-effect transistors with remarkably high electron mobility values of up to 6.50 cm(2) V(-1) s(-1) and with a high on-off current ratio of 10(5).