The aims of this study are (i) to demonstrate the synthesis of Cr3+-activated β-Ga2O3 films by metal-organic deposition and (ii) to report the temperature-dependent photoluminescence (PL) properties of such films from 20 to 300 K. An activation energy of ∼0.9 eV for the Cr3+ ions in β-Ga2O3 is determined from a plot of PL intensity vs calcination temperature. The red-line emission doublet R1 and R2 at ∼1.8 eV and the broad emission band with a peak at ∼1.7 eV are ascribed to the Cr3+ ions in the β-Ga2O3 host. The energies of the excited states, i.e., 2E, 4T2, 2T2, 4T1, and 4T1, in Cr3+ are determined from the experimental PL and PL excitation spectra using a newly developed analysis model. The high-energy luminescence tail of the broad 4T2 → 4A2 emission band can be explained by the hot-carrier effect of the photoexcited electrons in the 4T2 state. The relative intensities of the R-line emission doublet can also be explained very well by the population and depopulation of the electron numbers in the E¯ (R1) and 2A¯ (R2) states. PL properties, such as the temperature-dependent PL intensity, peak energy, and spectral width, are analyzed in detail.
No takes yet. Share an insight, caveat, or question.
Tokida et al. (2012) studied this question.
Synapse has enriched 2 closely related papers on similar clinical questions. Consider them for comparative context: