Transparent samples of cubic (8 mol % yttria) and tetragonal (3 mol % yttria) zirconia were prepared from nanometric powders by the pulsed electric current sintering process. The crystallite size of the resulting dense samples was about 50 nm in both cases. The consolidation pressure had a positive effect on the occurrence of transparency for both modifications. Transmittance in the near infrared for 1 mm thick samples is above the 60 % for the cubic (8 %YSZ) and above 50 % for the tetragonal (3 % YSZ) zirconia, representing between 70 and 80 % of the theoretical values of the two modifications. Samples had a yellowish‐brown coloration which was attributed to the presence of color centers. Annealing in oxygen improved transmittance initially, but prolonged annealing resulted in translucent samples. The role of porosity in transmittance is analyzed.
No takes yet. Share an insight, caveat, or question.
Anselmi‐Tamburini et al. (2007) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: