Investigation of Microphase Separation and Thermal Properties of Noncrystalline Ethylene Ionomers. 2. IR, DSC, and Dielectric Characterization

The microphase structure of noncrystalline poly(ethylene- co -13.3 mol % methacrylic acid) (E-0.133MAA) ionomers was investigated by using infrared (IR) spectroscopic, X-ray scattering, differential scanning calorimetric (DSC), and dielectric measurements. The noncrystallinity was confirmed by small-angle X-ray scattering (SAXS) and DSC studies, which has enabled a quantitative analysis of the SAXS ionic peak associated with ionic aggregates without being perturbed by the polyethylene lamellae peak. In 60% neutralized Na ionomer, it was revealed that almost 100% of MAA side groups including unneutralized COOH are incorporated into the ionic aggregates with an average ionic core radius ( R 1 ) of ∼6 Å. The dielectric relaxation studies showed that the ionic aggregates form a microphase-separated ionic cluster. Analysis of dielectric strengths indicated the most (∼90%) of the COONa groups are present in the ionic cluster. On the other hand, in the 60% neutralized Zn ionomer, both SAXS and dielectric studies indicated that the ionic aggregates with R 1 ∼ 4 Å are almost isolated and dispersed in the matrix; the formation of ionic cluster was not recognized. Similarly to partly crystalline E-MAA ionomers, all noncrystalline E-0.133MAA ionomers exhibited an endothermic peak at 320−330 K (labeled T i ) on the first heating, depending on the aging time at room temperature. Several factors that would be critical for the DSC T i peak were discussed. It was concluded that the DSC T i peak is certainly associated with changes of the state of ionic aggregate region.