Sequential crosslinking for mechanical property development in high sulfur content composites

This report details how sequential crosslinking processes can be applied to develop properties in sulfur‐bisphenol A composites. Olefinic carbons were first crosslinked by inverse vulcanization (InV) at 180°C and then aryl carbon crosslinking was affected via radical‐induced aryl halide‐sulfur polymerization (RASP) at 220°C. To demonstrate that these two crosslinking mechanisms are orthogonal and can be used to affect stepwise property changes, O , O ′‐diallyl‐2,2′,5,5′‐tetrabromobisphenol A was selected as a comonomer. After InV of the monomer with 90 wt% sulfur, a flexible plastic material having an elongation at break of 89% was obtained, whereas after heating this premade polymer to initiate RASP, the polymer develops a threefold increase in its tensile strength and has an elongation at break of only 29%. The sequential crosslinking strategy demonstrated herein thus provides an innovative approach to tuning the properties of high sulfur‐content materials.