Comparative Evaluation of the Fracture Resistance of Two Different Fiber-reinforced Composite Restorations with Particulate Filler Composite Restorations

Uncomplicated crown fractures are the most common form of traumatic dental injuries (TDIs) in children affecting their personal and social well-being. AIM: To evaluate the fracture resistance of fractured incisors restored with particulate filler composites, glass fiber-reinforced composites, and Polyethylene fiber-reinforced composite restorations. MATERIALS AND METHODS: Standardized incisal and mesio-incisal fractures with chamfer preparation were prepared on human maxillary central incisors. Test samples were restored using particulate filler composites (Filtek Z 250), glass fiber-reinforced composites (Fiber-Splint) and polyethylene-reinforced composites (Ribbond). Static load was applied to the test samples using Universal testing machine at a cross-head speed of 1 mm/min. Data were tabulated and analyzed using analysis of variance (ANOVA) (p = 0.05). RESULTS: Descriptive statistics of mean [standard deviation (SD)] peak failure load in incisal restorations for particular filler composite, glass fiber-reinforced composites, and polyethylene fiber-reinforced composites were 196.00 (± 67.46), 186.28 (± 66.44), and 246.71 (± 24.52) respectively, whereas for mesio-incisal restorations, mean (SD) peak failure loads were 169.28 (± 33.53), 218.57 (± 74.41), and 225.71 (± 57.52) respectively. CONCLUSION: Patnana AK, Rao VVN, Chandrabhatla SK, Rajasekhar VR. Comparative Evaluation of the Fracture Resistance of Two Different Fiber-reinforced Composite Restorations with Particulate Filler Composite Restorations. Int J Clin Pediatr Dent 2018;11(4):277-282.