Complete Decomposition of Li₂CO₃ in Li–O₂ Batteries Using Ir/B₄C as Noncarbon-Based Oxygen Electrode

Instability of carbon-based oxygen electrodes and incomplete decomposition of Li 2 CO 3 during charge process are critical barriers for rechargeable Li–O 2 batteries. Here we report the complete decomposition of Li 2 CO 3 in Li–O 2 batteries using the ultrafine iridium-decorated boron carbide (Ir/B 4 C) nanocomposite as a noncarbon based oxygen electrode. The systematic investigation on charging the Li 2 CO 3 preloaded Ir/B 4 C electrode in an ether-based electrolyte demonstrates that the Ir/B 4 C electrode can decompose Li 2 CO 3 with an efficiency close to 100% at a voltage below 4.37 V. In contrast, the bare B 4 C without Ir electrocatalyst can only decompose 4.7% of the preloaded Li 2 CO 3 . Theoretical analysis indicates that the high efficiency decomposition of Li 2 CO 3 can be attributed to the synergistic effects of Ir and B 4 C. Ir has a high affinity for oxygen species, which could lower the energy barrier for electrochemical oxidation of Li 2 CO 3 . B 4 C exhibits much higher chemical and electrochemical stability than carbon-based electrodes and high catalytic activity for Li–O 2 reactions. A Li–O 2 battery using Ir/B 4 C as the oxygen electrode material shows highly enhanced cycling stability than those using the bare B 4 C oxygen electrode. Further development of these stable oxygen-electrodes could accelerate practical applications of Li–O 2 batteries.