SmFeAsO and the isostructural superconducting SmFeAs(O 0.93 F 0.07 ) phase were prepared and characterized by means of Rietveld refinement of x-ray powder diffraction data, scanning electron microscope observation, transmission electron microscope analysis, and resistivity and magnetization measurements. Sintering treatment strongly improves the grain connectivity, but, on the other hand, induces a competition between the thermodynamic stability of the oxy-pnictide and Sm 2 O 3 , thus affecting the sample purity. In the pristine sample both magnetization and resistivity measurements clearly indicate that two different sources of magnetism are present: the former related to Fe ordering at T ∼140 K and the latter due to the Sm ions that order antiferromagnetically at low temperature. The feature at 140 K disappears in the F-substituted sample, and a superconducting transition appears, at low temperatures. The magnetoresistivity curves of the F-substituted sample probably indicate very high critical field values.
No takes yet. Share an insight, caveat, or question.
Martinelli et al. (2008) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: