The purpose of this study was to investigate the fretting fatigue crack initiation behaviour of titanium alloy, Ti–6Al–4V. Fretting contact conditions were varied by using different geometries of the fretting pad. Applied forces were also varied to obtain fretting fatigue crack initiation lives in both the low‐ and high‐cycle fatigue regimes. Fretting fatigue specimens were examined to determine the crack location and the crack angle orientation along the contact surface. Salient features of fretting fatigue experiments were modelled and analysed with finite element analysis. Computed results of the finite element analyses were used to formulate a shear stress‐based parameter to predict the fretting fatigue crack initiation life, location and orientation. Comparison of the analytical and experimental results showed that fretting fatigue crack initiation was governed by the maximum shear stress, and therefore a parameter involving the maximum shear stress range on the critical plane with the correction factor for the local mean stress or stress ratio effect was found to be effective in characterizing the fretting fatigue crack initiation behaviour in titanium alloy, Ti–6Al–4V.
No takes yet. Share an insight, caveat, or question.
Lykins et al. (2001) studied this question.
Synapse has enriched 5 related papers. Consider them for comparative context: