Conductive Electrospun Polyaniline/Polyvinylpyrrolidone Nanofibers: Electrical and Morphological Characterization of New Yarns for Electronic Textiles

This is the authors' abstract. We don't add key points for this paper.

Advanced functionalities textiles embedding electronic fibers, yarns and fabrics are a demand for innovative smart cloths. Conductive electrospun membranes and yarns based on polyaniline/polyvinylpyrrolidone (PANI/PVP) were investigated using the chemical modification of PANI instead of using conventional coating processes as in-situ polymerization. PANI was synthesized from the aniline monomer and the influence of the oxidant-to-monomer ratio on electrical conductivity was studied. The optimized conductivity of pellets made with pressed PANI powders was 21 S·cm−1. Yarns were then prepared from the t-Boc-PANI/PVP electrospun membranes followed by PANI protonation to enhance their electrical properties. Using this methodology, electrospun membranes and yarns were produced with electrical conductivities of 1.7 × 10−2 and 4.1 × 10−4 S·cm−1.