Development of Cu particles and Cu core-shell particles reinforced Al composite

Copper particles were incorporated and retained in elemental state in an aluminium matrix by friction stir processing thereby producing a non-equilibrium particulate composite. The processed Al–Cu p composite exhibited improved strength with significantly high ductility. The composite was stable up to a temperature of more than 300°C. Thermal exposure at 350°C for more than 10 min led to diffusion of Cu atoms into the Al matrix forming a core-shell type structure in the Cu particles and thus producing an Al–Cu core-shell composite. The shell consists of multiple layers, the thickness of which was controllable.